Causes and control

Shrinkage and cracking in high-performance concretes –

Introduction

The problem of load-independent cracking in concrete members is as old as the construction method itself. Cracking is primarily caused by thermal, hygric and chemical processes as well as their superposition in the hardening and hardened concrete. Innovations in concrete technology, such as innovative admixtures or binding agents for high-performance concretes, have, in part, aggravated the risk. Since the primary crack formation processes are nowadays largely understood, the risk of cracking can be effectively counteracted. This paper discusses shrinkage of high-performance...

Related articles:

Issue 02/2015 New findings and calculation methods

Creeping and shrinking of ultra-high performance concrete (UHPC)

Due to their high strength and durability, ultra-high performance concretes allow realizing particularly exposed building structures. The fact that despite its dense microstructure UHPC is subject...

more
Issue 10/2009 Precast columns

New possibilities of concrete technology

Columns for high-rise buildings which have high demands on the architectural perception (Fig. 1) are often constructed as composite steel columns. This construction method enables the design of...

more
Issue 02/2014 On early and late restraint stresses

Designing cracks properly

Structural engineers are often uncertain about how to deal with the concept of restraint stress. Relevant codes and standards are of no help either. For relevant information, they have to refer to...

more
Issue 07/2010 Development of a new testing machine

Testing of fiber-reinforced concretes

The steel fibers are strongly bonded in the cement paste (structure) during the curing process of the concrete. The result is a remarkably higher compressive strength and in particular concerning the...

more
Issue 10/2020

Compressive strength classes and performance classes of ultra-high-performance concrete (2)

3 Classification of UHPFRC in tension 3.1 Parameters and test method The axial post-cracking tensile strength (notation: fcft) is the most important material parameter of ultra-high-performance...

more